Why After Spraying Has Poor Leveling Performance, With Obvious Orange Peel? 1. Coating is toothick or too thin Solution: Control the coating thickness by adjusting the coating equipment2. Baking temperature is too low Solution: Adjust the baking temperature to the correct value

It is prepared by using special resin with high cross-link density as the main raw material, which has excellent weather resistance, salt spray resistance and excellent abrasion resistance, and is specially used for the outer layer of aluminum wheels and high-grade bathroom anti-corrosion coating, a

On March 10, the commendation meeting of Yajia Group's 2022 advanced operation team and an excellent salesman and the signing of the 2023 annual management target responsibility letter were successfully held in Yichang, the "Hydropower Capital of the World". The shareholders of the board of direc

Celebrating the participation of Yajia Branch-Liaoning Branch in Liaoning City Exhibition

The 15th year since the founding of Yajia Group by Apr. 18,2022. It's not easily when the epidemic still serious that the leaders of Group and all of the employees gathered to celebrated the milestone moment,certainly it should be compactly. Mr Wang Guixiang as the president of Group has reward tot

1. The coating film is too thin lncrease the coating thickness of the coating film 2. Uncleanspraying environment The spraying room should be clean, the air should be purified, and theworkshop should be kept clean. 3. Unclean baking environment (A) control the amount of air

Solution of Bubbles or Pin-holes in epoxy coatings?1. Workpiece degreasing and rust removalis not complete or phosphating after washing is not clean The strict control of surfacetreatment quality 2. Moisture not thoroughly dried after surface treatment Appropriately

1. Excessive baking time Shorter baking time, our standard time is 200'C/10Mins 2. Excessivebaking temperature Lower baking temperature 3. Uneven coating thickness Pls reference.4. Unclean air in the oven Check air heating system and exhaust air 5. Powder formulation needs

1. Pre-treatment Sandblasting and sanding to ensure that the workpiece is free of oil andembroidery. 2 . Theoretical curing conditions of powder coating A. Theoretical curing condition130°C/20min. 160°C/15min. 180°C/10min. 200°C/5min. B. Temperature is the actual